PROPERTY
|
ASTM Test Method
|
*NOMINAL VALUES
|
| ~ |
~ |
SI UNITS |
ENGLISH UNITS |
| Density (Natural) |
D1505 |
0.946 g/cc |
-- |
| Density (Black) |
D1505 |
0.957 g/cc |
-- |
| Flow Rate (190/21.6) |
D1238 |
8.5 gm/10 min. |
-- |
| Tensile Strength @ Ultimate |
D638 |
34.5 MPa |
5,000 psi |
| Tensile Strength @ Yield |
D638 |
24.1 MPa |
3,500 psi |
| Ultimate Elongation |
D638 |
>800% |
>800% |
Flexural Modulus
(2% Secant) |
D790 |
938 MPa |
136,00 psi |
Environmental Stress Crack
Resistance (ESCR) |
~ |
~ |
~ |
| Fo' Cond. C |
D1693 |
>10,000 hrs. |
>10,000 hrs. |
| Compressed Ring ESCR, Fo |
F1248 |
>10,000 hrs. |
>10,000 hrs. |
| Brittleness Temperature |
D746 |
< -117oC |
< -180oF |
| Vicat Softening Temperature |
D1525 |
124oC |
255oF |
| Impact Strength (Notched) |
D256 |
0.37/KJ/m (7ft.-lb./in.) |
0.53/KJ/m (10ft.-lb./in.) |
| Hardness Shore D |
D2240 |
64 |
64 |
| Thermal Expansion |
-- |
2x10-4 cm/cm/oC |
1.1x10-4 in./in./oF |
|
|
| Cell Classification: |
D3350 |
345444C |
Grade PE34 |
| Material Classification: |
D1248 |
Type III
Category 5 |
Class C |
| PPI Hydrostatic Design Basis: |
D2837 |
11.0MPa (1600 psi) @ 23oC |
1600 psi @73.4oF |
|
|